Abstract:

OBJECTIVE:
The aim of this in vitro study was to evaluate the bond strength of a new calcium silicate cement, Neo MTA Plus (Avalon Biomed Inc. Bradenton, FL, U.S.A) by comparing ProRoot MTA and Biodentine. Material and Methods: Sixty dentin slices were instrumented to achieve a diameter of 1.3 mm. Group 1: white ProRoot MTA, group 2: Biodentine, group 3: Neo MTA Plus – G (powder mixed with gel), group 4: Neo MTA Plus – W (powder mixed with distilled water) were loaded into cavities. The push-out bond strength values were measured. Data were analyzed using Welch ANOVA with Bonferroni correction p = 0.05. Failure modes (adhesive, cohesive, and mixture) were analyzed.

RESULTS:
The highest bond strength value was recorded in Neo MTA Plus mixed with gel (5.23 Å} 1.78 MPa), whereas white ProRoot MTA (2.57 Å} 0.66 MPa) had the lowest. Bond strength values of Neo MTA Plus mixed either with gel or with distilled water were statistically different from both white ProRoot MTA and Biodentine (2.61 Å} 0.70 MPa) (p < 0.05). Adhesive failure was predominantly observed in all groups.

CONCLUSION:
Neo MTA Plus could be considered as alternatives to the ProRoot MTA and Biodentine due to its better performance in bonding to root dentin.

Journal of Adhesion Science and Technology.2016, Sept. DOI: 10.1080/01694243.2016.1219443

Sevinç Aktemur Türker, Uzunoğlu, Emel & Bilgin, Burcu